We’ve been commitment to offer the competitive rate ,outstanding merchandise good quality, too as fast delivery for Manufactur standard Tungsten Trioxide/Tungsten (VI) Oxide /Tungsten China/Wo3, On account of superior quality and competitive selling price , we’re going to be the current market leader, be sure to don’t wait to contact us by mobile phone or email, in case you are fascinated in any of our products.
We’ve been commitment to offer the competitive rate ,outstanding merchandise good quality, too as fast delivery for China Tungsten Trioxise, Tungsten Oxide, Our company has built stable business relationships with many well-known domestic companies as well as oversea customers. With the goal of providing high quality products and solutions to customers at low cots, we’ve been committed to improving its capacities in research, development, manufacturing and management. We’ve honored to receive recognition from our customers. Till now we’ve got passed ISO9001 in 2005 and ISO/TS16949 in 2008. Enterprises of “quality of survival, the credibility of development” for the purpose, sincerely welcome domestic and foreign businessmen to visit to discuss cooperation.
Parameter:

Feature:

-High heat insulation, good transparency, when infrared blocking rate 99%, visible light transmittance can reach more than 70%;
-It has good universality, can be matched with most resin such as acrylic resin and UV resin;
-We owns a number of independent intellectual property rights on it, therefore advantages in technology and price;
-Strong weather resistance, QUV 5000 h, no attenuation in performance, no change in color;
-Safe and reliable, free of toxic and harmful substances such as halogen, heavy metals.

Application:

It is used to make high performance insulation window film, which can be used for automobile and building glass to get heat insulation, energy saving, improving comfort, or it is used in other fields with the requirement of heat insulation or anti-infrared.

Usage:

Note: Small sample test with resin is necessary before use.

Step 1: Taking out the below material by weight ratio: GTO solution: diluting agent: PSA resin=1.5:4:4. Adjusting the GTO dosage according to the parameter requested (7099) with testing machine with 950nm.

Diluting agent: the mixing of EA:TOL =1:1

Step 2: Mixing. Mix them one by one: adding GTO solution — adding diluting agent — stirring — adding PSA resin while stirring. Stirring for about 40min after adding PSA, and then filtering the mixture with 1um filter cloth.

Step 3: Choosing PET basic film. Choose the PET basic film with VLT over 90% and corona layer.

Step 4: Coating. Coat them (the mixture in step 2) on the PET film by wet film coating machine.

Step 5: Drying, laminating. Controlling the coating thickness between 6-8um, drying Temperature: 85~120 deg.

Notes：

1. G-P35-EA can’t be added for reverse adjustment during the batching process or after the ingredients are finished.

2. In every mixing, the order of addition must be abided strictly, especially that the mixing tank can not be used without cleaning thoroughly, even a small amount of residual working fluid will lead to serious problems such as graininess precipitation.

3. When cleaning the pipeline and related equipment, the special diluent has to be used.

Notes：

1. Keep sealed and store in a cool place, make the label clear to avoid misusing.

2. Keep far from the fire, at the place where children can’t reach;

3. Ventilate well and prohibit the fire strictly;

4. Wear PPE, such as protective clothing, protective gloves and goggles;

5. Prohibit contacting with the mouth, eyes and skin, in case of any contact, flush with large amount of water immediately, call a doctor if necessary.

Packing:

Packing:1kg/bottle; 20kg/barrel.

Storage: in a cool, dry place, avoiding sun exposure.