Professional China China 100% Anti-UV&IR Low-R Heat Insulation Laminated Building Glass for Curtain Wall
Every single member from our higher effectiveness product sales staff values customers’ requires and organization communication for Professional China China 100% Anti-UV&IR Low-R Heat Insulation Laminated Building Glass for Curtain Wall, We hope we are able to have a pleasant partnership with businessman from all over the environment.
Every single member from our higher effectiveness product sales staff values customers’ requires and organization communication for China Clear Laminated Glass, Colored Laminated Glass, We have now to continue to uphold the “quality, complete, efficient” business philosophy of “honest, responsible, innovative”spirit of service, abide by the contract and abide by reputation, first-class solutions and improve service welcome overseas customers patrons.
This product is developed based on ATO, prepared by mixing other metal oxide. It has good transparency, and the performance of blocking near infrared is much better than that of ATO and ITO below 1000nm, that is the most sensitive area of heating effect for human skin. The heat insulation window film that produced by the medium can greatly improve the comfort of human body and save electric energy greatly, make people enjoying warm in winter and cool in summer, which provides technical guarantee for creating a more comfortable, eco-friendly and energy-saving indoor environment.
-It has good universality, can be matched with most resin such as acrylic resin and UV resin;
-We owns a number of independent intellectual property rights on it, therefore advantages in technology and price;
-Strong weather resistance, QUV 5000 h, no attenuation in performance, no change in color;
-Safe and reliable, free of toxic and harmful substances such as halogen, heavy metals.
Note: Small sample test with resin is necessary before use.
Step 1: Taking out the below material by weight ratio: GTO solution: diluting agent: PSA resin=1.5:4:4. Adjusting the GTO dosage according to the parameter requested (7099) with testing machine with 950nm.
Diluting agent: the mixing of EA:TOL =1:1
Step 2: Mixing. Mix them one by one: adding GTO solution — adding diluting agent — stirring — adding PSA resin while stirring. Stirring for about 40min after adding PSA, and then filtering the mixture with 1um filter cloth.
Step 3: Choosing PET basic film. Choose the PET basic film with VLT over 90% and corona layer.
Step 4: Coating. Coat them (the mixture in step 2) on the PET film by wet film coating machine.
Step 5: Drying, laminating. Controlling the coating thickness between 6-8um, drying Temperature: 85~120 deg.
Notes：
1. G-P35-EA can’t be added for reverse adjustment during the batching process or after the ingredients are finished.
2. In every mixing, the order of addition must be abided strictly, especially that the mixing tank can not be used without cleaning thoroughly, even a small amount of residual working fluid will lead to serious problems such as graininess precipitation.
3. When cleaning the pipeline and related equipment, the special diluent has to be used.
Notes：
1. Keep sealed and store in a cool place, make the label clear to avoid misusing.
2. Keep far from the fire, at the place where children can’t reach;
3. Ventilate well and prohibit the fire strictly;
4. Wear PPE, such as protective clothing, protective gloves and goggles;
5. Prohibit contacting with the mouth, eyes and skin, in case of any contact, flush with large amount of water immediately, call a doctor if necessary.
Packing:
Packing:1kg/bottle; 20kg/barrel.
Storage: in a cool, dry place, avoiding sun exposure.